Preparation and Properties of Graphite/Epoxy Resin Conductive Composites
Published: |
May 30, 2023 |
Author: |
Shan-Shan Yao, Di Jiang, Qi-Zhong Zhang, Xin-Xin Wang |
Abstract: |
Graphite / epoxy resin conductive composites were prepared by mixing and molding process, using graphite and epoxy resin as raw materials, filling carbon fiber cloth and mixing a small amount of metal powder. We investigated effects on the different ratio of graphite raw materials and the amount of carbon fiber cloth and different metal powder on the resistance and bending strength of graphite / epoxy resin conductive composites. The optimum ratio of raw materials was determined by the experiment. The results showed that the electrical and mechanical properties of the composites were good when the ratio of the two kinds of graphite was 1:1, filling two layers of carbon fiber cloth and the content of aluminum powder was 1%. The resistivity was up to 0.0800 ohm cm, and the bending strength was up to 47.32MPa. ... |
You must be a registered user to talk back to us. |
Company Information:
More SMT / PCB assembly technical articles »
- Mar 19, 2024 - What is Underfill | GPD Global
- Mar 19, 2024 - Made in Japan: Solder Paste Jet Dispensing Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 26, 2024 - Precision Control in Electronic Assembly: Selective Wave Soldering Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 02, 2024 - Maximizing Efficiency: The High-Speed SMT Line With Laser Depanelizer | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Dec 27, 2023 - Revolutionizing Tech: SMT Auto IC Programming Machine Mastery | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Browse Technical Library »
Preparation and Properties of Graphite/Epoxy Resin Conductive Composites article has been viewed 150 times