Electronics Forum | Mon Jun 17 17:04:15 EDT 2002 | pjc
Guys, Thanks for the input. Its a Opto-Electronic project I'm working on for a customer with a device on a ceramic substrate. Yes, I did learn from Indium that 007 is no-clean and has a high-solids content. They reccommended using TacFlux 010, which
Electronics Forum | Fri Aug 16 11:03:22 EDT 2002 | Claude_Couture
I use Kyzen's Aquanox SSA cleaner in a heated parts cleaning tub to clean anything with flux condensate on it. When heated to 120F, the stuff melts away like ice under hot water. When the cleaning solution is loaded, I send it in an evaporator. The s
Electronics Forum | Thu Jul 31 11:33:51 EDT 2003 | yngwie
I faced problem over connecter's pin that were hot air soldered. This connector has 168 pins ( similar to the straddle connector ). The process is to apply the flux onto the connector's J-leads, and the hot air pencil were then ran thru' the leads to
Electronics Forum | Mon Feb 28 13:13:25 EST 2005 | russ
ING, you had to nake it difficult didn't ya! It appears that all of your parameters are okay. When you state that "sometimes there is a residue" is it liquidous or dry? Is your spray fluxer an ultrasonic or a spray gun head? You may not be getting
Electronics Forum | Wed Aug 17 22:41:37 EDT 2005 | davef
Peter are you having fun with solder masks erwat? We saw this years ago with LPI solder masks. It shows occasionally with other masks. We agree with Russ. If nothing [eg, alcohol, flux thinner, acetonitrile, or water] dissolves the haze, then it
Electronics Forum | Fri May 14 12:01:40 EDT 1999 | Chrys Shea
| | | I am looking for anyone who has converted over to VOC Free flux. I need some info on any problems, etc. that you might have had. | | | | | | Please E-mail me at wes.ruggles@vickers-systems.com or call at (513) 494-5229 | | | | | | Thanks | |
Electronics Forum | Mon Feb 28 12:17:49 EST 2005 | lyrtech
TO JAY: What type of assemblies are you having 50-75% fill on. - Capacitor, resistor Are they single sided? - Yes Plated through hole? - No Is this a recent problem? - Yes, first time, but we don't know how long it last. TO RUSS: What is your t
Electronics Forum | Mon Feb 27 17:08:15 EST 2006 | GS
3,5 ugr/cm2 NaCl) or power components, or Raw PCB. Nothing with the solder process or fluxes. Ion Chromatography analysis was necessary to help understanding of contamination origin. When occasionally we run TIC on a NC assembled PBA (Paste ROL0 or
Electronics Forum | Fri Jan 15 03:30:10 EST 1999 | Jeff Sanchez
| Hi all, | | I thought I'd use this forum to ask a couple general questions on fluxes for manual operations: | First - Is it OK to use a wave soldering type flux (specifically OA)? Thinking about activation temperatures and the ramp rate of the wav
Electronics Forum | Wed Jan 10 17:18:11 EST 2007 | flipit
I am soldering a Germanium Window with a > metalized rim to a Ni-Au plated kovar lid. The > solder joint needs to be hermetic. I am using > 80In solder washer shape preform, but am > experiencing lots of voiding when x-rayed, > although the jo