Electronics Forum | Sun Apr 05 09:46:47 EDT 1998 | Earl Moon
| We are looking at reflow soldering some Flexi-rigid | pcbs. I have heard that IR reflow soldering can make the Polyimide "self heat" and cause de-lamination. | Does anyone have any info. The thermal problems associated with polyimide rigid/flex de
Electronics Forum | Tue Jun 02 14:32:58 EDT 1998 | Chris Fontaine
We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not alwa
Electronics Forum | Sat Nov 22 09:27:18 EST 2008 | davef
IPC-HDBK-001 w/Amendment 1 Handbook and Guide to Supplement J-STD-001 (Includes J-STD-001B to C Comparison). During fabrication and storage, both components and PWBs will often absorb water. If left in the device, this water will vaporize at solderi
Electronics Forum | Wed Jun 03 01:06:13 EDT 1998 | Mike Moninger
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al
Electronics Forum | Wed Jun 03 07:13:27 EDT 1998 | Tom Tellinghuisen
| We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not al
Electronics Forum | Wed Jun 03 15:22:12 EDT 1998 | Greg Curler
| | We have experienced poor adhesion of acrylic conformal coating to plastic bodied IC�s. The observed symptoms of this are a blistering or lifting of the coating at the surface of the component, although peel testing has revealed that this is not
Electronics Forum | Tue Feb 03 13:39:08 EST 2009 | grics
Good morning Jamie. I work at a CM and can offer some input on process flexability. I do not have any data on how reliable the coating is but I can say that they are both very difficult to control. Will you be selective coating or full coating? Ho
Electronics Forum | Mon Nov 27 13:36:41 EST 2000 | C.K.
You'd more than likely have repairability issues with the Acrylic based one. The acrylic-based finish is alot harder and more brittle versus the silicone. Some of the new silicones, you can just "peel" with your fingernail, while still getting reli
Electronics Forum | Thu Feb 25 10:21:49 EST 2010 | jdumont
My guess would be that the adhesive used on the dots contains silicone. We use 1B73 which is also acrylic and it hates silicone. We use silicone RTV to permanently mask around some connectors and unless its fully cured before coating it will cause l
Electronics Forum | Mon Dec 27 10:03:35 EST 2010 | duso02
Contact your distributor for the coating or Humiseal directly. Humiseal has had a recent issue with batches of 1B31. The specific problem is lack of adhesion, which is what you have as well. You need to find out if your batch # is one of the affected