Electronics Forum | Tue Sep 22 12:58:18 EDT 1998 | Chyrs
| How can I solve the small solder ball in the N2 W/S ? | The Oxygen level is 10000~20000ppm & no-clean flux. Yuen, Sorry I an't got an answer, just more questions. 1-2% O2 in your wave solder - are you running membrane generated nitrogen? I don't
Electronics Forum | Tue Jan 23 20:53:51 EST 2001 | davef
Sorry, not much help for me there. More information would be helpful. For instance: * Talk about the distribution of the problem, including a single lot or from various lots and over components and component types on the board * Tell us about the boa
Electronics Forum | Mon Jul 03 05:39:05 EDT 2006 | ronalds
Hi, I am experience problems while testing wave soldering SMT components that are glued on the solderside (lead free). Between de leads of SOx type IC's and SOT's develop a great deal of solder beads. I have been using a RSS temp.profile while spr
Electronics Forum | Mon Dec 06 08:55:11 EST 1999 | Dave F
Vinesh: The white residue is perfectly expected, when washing a no-clean with water (and some alcohol). In some cases, the white resin that you are seeing can be removed. Your paste supplier should be able to provide details. Recognize that clean
Electronics Forum | Fri Jan 14 12:20:12 EST 2011 | SheanDalton
There is a lot of information available about cleaning no-cleans. Takes chemical, mechanical and thermal energy. Find the right chemistry for the flux (not something like IPA that will most likely just smear the residues around and cause problems
Electronics Forum | Mon Jun 25 20:54:28 EDT 2001 | davef
No, I�m suggesting an increase in the distance between the two pads on the board. This "G" in SM-782A "Surface Mount design & Land Pattern Standard" parlance. You shouldn�t fight solder balls for long periods. You should just increase the pressure
Electronics Forum | Wed Dec 08 14:44:13 EST 1999 | John Thorup
Hi Chuck We make precision analog and hybrib audio processing equipment for the radio and TV broadcast industry. We have not experienced any problems relating to no-clean reflow since the introduction of the process several years ago. It is known t
Electronics Forum | Tue Jul 19 09:18:14 EDT 2011 | davef
Could this be an opportunity to explore the use of cartridge-type paste dispensers? Or maybe a reason to keep working over the weekend. * Re-Storing & Re-Using “Used” Solder Paste. Though not a recommended practice, used solder paste from the stenci
Electronics Forum | Wed Jul 13 15:26:32 EDT 2005 | russ
The problems we saw had to due with the Flux I believe. We saw what I would call poor coelescence and the residues were very hard for us to clean with our Water only cleaner. I will not lie and say I worked on the process very much. Since we alrea
Electronics Forum | Thu Jul 15 18:50:43 EDT 1999 | Raeto Zryd
We intend to use VOC free fluxe in our nytro machine. Does anybody know if there can be problems with water ie. solvent residues in the tunnel. Perhaps there are some white papers available on that issue.