Electronics Forum | Thu May 06 18:06:43 EDT 1999 | JohnW
| | Can anyone pls email me a typical temperature profile for wave soldering process. | | | | Thank you vey much. | | | | rdgs... | | | Typical depends on the processes you're developing. | | Key factors in my experience are flux type and requi
Electronics Forum | Thu May 06 18:07:59 EDT 1999 | JohnW
| | | Can anyone pls email me a typical temperature profile for wave soldering process. | | | | | | Thank you vey much. | | | | | | rdgs... | | | | | Typical depends on the processes you're developing. | | | | Key factors in my experience are f
Electronics Forum | Tue Jul 24 13:15:22 EDT 2001 | Steve Schrader
Greg, The increased space and hence potentially increased airflow will have no effect on "solderability." It may effect the temperature that the balls see and that is a different issue that can be worked from a profile standpoint if you are not hit
Electronics Forum | Mon Sep 26 01:44:51 EDT 2005 | vinc
Just be aware of what Japanese had done. They do not stick to one alloy as it is impossible and depends on the constraint you are facing with. As for Hitachi, according to one advertisment put up in SMT magazine seems to me that they are going for
Electronics Forum | Mon Aug 21 04:36:34 EDT 2006 | Rob
Yes, appropriate storage & component handling proceedures should be followed depending on the MSL (Moisture Sensitivity Level) class of the component. Some component suppliers are now marking the MSL class on the label, along with PBT (Peak Body
Electronics Forum | Mon Jul 14 11:33:35 EDT 2008 | stepheniii
It depends on the type of iron. Some of ours have a little plug you pull out that exposes a pot that you tweak to make the temperature of the tip the same as the reading. Others can't be adjusted and the heating element must be replaced if they don't
Electronics Forum | Wed Sep 05 16:35:22 EDT 2012 | davef
It depends, but I'd guess that as a minimum the floor clock will start when the component returns to room temperature. It's easy to argue that the floor clock starts earlier than that!!! Probably, the floor clock starts a couple degrees lower than th
Electronics Forum | Wed Jul 10 14:14:21 EDT 2013 | benreben
hi all, i have purchased an used vapor phase and i can't make a constant profile. the profiles depend on the time i wait between two batch... the only difference that i include is the chamber temperature i don't understand why the chamber temperat
Electronics Forum | Sat Jul 22 14:50:04 EDT 2017 | spitkis2
It depends on the thermal mass of your assemblies (boards and components). Generally, if boards are small with few layers, the additional mass of components may have a significant impact on reducing the peak temperature. If boards are larger with s
Electronics Forum | Mon Nov 27 17:50:01 EST 2000 | Dave F
Mike: It gets more humid in the winter? [I can see it�s true (not that I�d doubt you) cause I�m looking a a humidy map of the USA, right now] How does that work outin Californy? [Do the ocean breezes move the humid air in-land in the summer? Er w