Electronics Forum | Thu Sep 23 11:56:30 EDT 2004 | rkevin
We are printing on an assembly using SAC305 Alloy Sn96.5 Ag 3 Cu .5 with a no clean flux and getting virtually NO spread with either a ramp to spike or straight ramp profile. We are printing to standard FR4 board with immersion Ag finish. I am trying
Electronics Forum | Tue Dec 14 18:03:22 EST 2004 | Dreamsniper
Hi, Can you guide with the above? I read ROSE Test is a process control tool. What about Ion Chromatography, SIR and FT-IR. What Accpetance Criteria will I use for our assembly when using WS Flux? My WS Flus says it has 0% Halide so What can Ion Chr
Electronics Forum | Tue May 09 21:53:06 EDT 2006 | KEN
What is your flux delivery system? Tell us a little more....please. I'm assuming ultrasonic. You can try to vary your air knife but if your pin / hole ratios are wrong then it may not help. Run a bare fab. If your problem goes away you may need to
Electronics Forum | Mon Oct 13 08:43:56 EDT 2014 | rob
Hi Larry, Picture a old lady with a set of knitting needles with leads attached to them, pressing the needles into different points of the PCB (pads, test points or component leads) and measuring resistance, inductance, waveforms etc between these p
Electronics Forum | Fri Oct 19 13:57:17 EDT 2007 | Michael Konrad
Hi Rob, I must take issue with your statement �By definition, no clean solder can be not-cleaned�. All no-clean fluxes can be cleaned. Whether or not one cleans no-clean depends on a variety of factors. More than eighty percent of all post reflow
Electronics Forum | Wed Oct 10 08:01:28 EDT 2007 | ck_the_flip
We use Indium 1074-EXR on ERSA, and it's performed miracles on our yields. Spot soldering, like wave, is all about fundamentals. Put just enough flux, preheat to prevent thermal shock and activate the flux, and then solder with enough dwell time to
Electronics Forum | Wed Jan 27 21:02:53 EST 1999 | Dave F
| i am working with the noclean process and getting white residues on the bottomside of the board probably due to the | wave soldering flux.i am using a no-clean solder paste and a noclean wave solder flux.The boards passed the accelerated temperatu
Electronics Forum | Mon Jun 28 10:03:22 EDT 2004 | davef
First, welcome to your new job. Second, IPC-TM-650 2.6.14 is only loosely an �Ionic Contamination (Electromigration) Test�. * Electromigration Test, IPC TM 650 2.6.14, 2.6.14.1 * Ion Chromatography for Ionic Cleanliness, IPC TM 650 2.3.28 Third, I
Electronics Forum | Mon Mar 29 11:49:44 EST 2004 | gregoryyork
White residue, probably nothing to do with the flux but was more than likely mineral salts from resist cure problem that are only soluble in Mineral Acids. No residue is the best IF resist is good, if resist issue's use low solids Rosin No Clean and
Electronics Forum | Wed Oct 11 09:55:10 EDT 2000 | Ian Harrison
Some boards that are populated by one of our subcontractors are getting a white powdery residue forming on them. I think it is the non clean flux and process which they are using that is causing the problem. Their process is as follows. Flux is put i