Electronics Forum | Fri Sep 12 04:21:54 EDT 2008 | gsala
Had same problem with SOT23 (two different PNs and Suplliers) problem was random (AVG 0,15%). Parts are RoHS but soldered by SnPb, Lead frame Plating (e3)according to IPC-J-STD609 it means Sn pure (check the label on reel), additional info, it is S
Electronics Forum | Mon Nov 24 11:19:21 EST 2008 | sjones
I am having problems soldering a Rohs compliant BGA ATMEL AT91RM9200(rohs compliant board) This device recommends a soldering profile from J-STD-20 and a minimum peak package temperature of 250 centigrade,peak 260. However a lot of the other componen
Electronics Forum | Mon Nov 24 11:26:08 EST 2008 | sjones
I am having problems soldering a Rohs compliant BGA ATMEL AT91RM9200(rohs compliant board) This device recommends a soldering profile from J-STD-20 and a minimum peak package temperature of 250 centigrade,peak 260. However a lot of the other componen
Electronics Forum | Wed Feb 04 09:58:50 EST 2009 | dyoungquist
As was stated before, you need to have oven temperatures (profile) set such that you get good solder joints with the paste you are using. And definately run a profiler through yor oven to verify it is working properly. As for components, most data
Electronics Forum | Tue May 12 01:09:17 EDT 2009 | malmsteen
Thanks for replying Mr BoardHOuse. The product has to be RohS compliance. Surface finished is something that I am still considering and currently looking at either OSP or Immesion Silver. In short whatever combination that can produce high reliabili
Electronics Forum | Fri Nov 13 06:56:37 EST 2009 | CL
Good Morning, The customer is looking for void free connections. They had never specified an acceptable percentage. We are reacting to the test yield. Our yield has averaged 50%. We do not test the product so we rely on feeback from the customer. Us
Electronics Forum | Fri Feb 05 14:39:50 EST 2010 | gregcr
Hi All, We evaluated and approved KESTER R520A for our default RoHS solder paste a couple years back. It's time to re-evaluate to see if this material is still the best choice. Please let me know your opinion on the solder paste you are using, and
Electronics Forum | Mon Oct 18 11:43:42 EDT 2010 | hegemon
Use the forums nice search feature above. "Lead Free BGA" Lots of info. In short it seems the general consensus is that you are pretty much safe using your lead free BGA in a tin lead process, provided you run your peaks a little higher, and your
Electronics Forum | Thu Oct 31 17:34:37 EDT 2013 | hegemon
Keep in mind that you may need to assure that there are no pure tin finishes remaining on your parts. A general idea is that parts with pure tin (RoHs) finish will need to be plated with tin-lead solder to avoid the possibility of tin whiskers formi
Electronics Forum | Tue Oct 25 11:48:03 EDT 2016 | dontfeedphils
Hi, we're currently running a design with a fairly simple BGA. The problem we're running into is poor solderability (cold looking joints, high voiding in the BGA). All of this on a know good oven, with a known good thermal profile. I'm guessing it