Electronics Forum | Thu Jan 28 08:58:10 EST 1999 | Peet
| | i am working with the noclean process and getting white residues on the bottomside of the board probably due to the | | wave soldering flux.i am using a no-clean solder paste and a noclean wave solder flux.The boards passed the accelerated tempe
Electronics Forum | Wed Dec 27 20:33:50 EST 2006 | greg york
water alone especially cold is not good enough, how do you check for hasl fluids when most residues left behind after improper cleaning are non ionic. Use 40C saponifier followed by heated rinse then cold rinse then DI rinse followed by dry.Nylon bru
Electronics Forum | Thu Jul 07 15:32:37 EDT 2005 | saragorcos
Hi Lloyd, Have you done any ionic analysis to find out what the flux residue is composed of? If you can eliminate the source residue, then your problem obviously should go away. Though tombstoning isn't known to be much of a functional problem it i
Electronics Forum | Sun Sep 07 17:16:57 EDT 2008 | gregoryyork
OK Pizza it is then, here goes. Dewetting of Ni/Au pads, paste favouring the Tinned component lead hence excess paste wicking on top of the components. Reason is EITHER Nickel migration into the gold due to high levels of Ionics from poor rinse OR mo
Electronics Forum | Thu Jan 28 09:45:44 EST 1999 | parag
| | i am working with the noclean process and getting white residues on the bottomside of the board probably due to the | | wave soldering flux.i am using a no-clean solder paste and a noclean wave solder flux.The boards passed the accelerated tempe
Electronics Forum | Mon Apr 15 22:37:27 EDT 2002 | davef
Regarding your customer suditor, it would have been nice if you said something like ... Routinely, our testing shall be less than 1.56 microgram/cm^2 NaCl equivalent ionic or ionizable flux residue, according to TM-650, Method 2.3.35 'Detection And
Electronics Forum | Thu Jul 25 21:49:55 EDT 2002 | davef
Consider: * Quitting the coating business all together and using a coating service supplier, like: Thermospray Co 800-952-5838 Mike Moninger; Advanced Coating 800-722-1444; Epsco 108 W. 37th St Boise Idaho 83714 (208)389-2000 * Buying a programmable
Electronics Forum | Tue Nov 04 19:34:27 EST 2003 | gregoryyork
Blimey that's a problem and a half. Water Solubles will look completely different residue wise than No Cleans, pending age and solids contents No Cleans will go white powdery - watersolubles will stay oily Alternatively process reworked PCB's through
Electronics Forum | Mon Jan 08 20:57:52 EST 2001 | Dave F
Are you talking about bare board cleanliness or assembly level cleanliness? Bare board cleanliness is still primarily measured by resistivity of solvent extract (ROSE) using instruments such as Omegameters and Zero Ions. What is considered as "acce
Electronics Forum | Mon Jun 11 22:06:00 EDT 2001 | davef
The issue is not the cleanliness of your in-bound water. The issue is the cleanliness of the board your customer receives. Look at J-STD-001C, Para 8, "Cleanliness Requirements". The end product cleanliness is the end result of your: * In-bound