Electronics Forum | Fri Sep 17 15:01:05 EDT 1999 | Dave F
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Fri May 12 12:07:10 EDT 2006 | solderiron
The kester better known as KY'd Sn/Cu has more copper intermetallic growth over time, dissolves copper from the board faster so repairing and touchup can damage board. Bridges more than SN100c. Does not thermal cycle well. Has shrink cracks that can
Electronics Forum | Thu Nov 08 10:52:22 EST 2012 | Bryan Ng
I am considering using high-temp ball Sn10Pb90 + eutectic solder paste for MLC reflow (no underfill). You can see that there is no Intermetallic bond for the paste and the balls. Under high stress/shock condition, the solder joints develop micro c
Electronics Forum | Fri Sep 17 06:01:12 EDT 1999 | Earl Moon
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Wed Feb 02 20:53:34 EST 2000 | Dave F
Dennis: Several points: 1 If you're talking AlphaLevel process (?): � Good solderability, as HASL, even no-cleans bite well. � Planarity, uniform deposit, no bridgin� of FP. � Doesn't store as well as NiAu ... LT 6 months sealed � Very sensitive t
Electronics Forum | Thu Jul 03 07:43:50 EDT 2003 | davef
So, there is a crack or gap between: * Solder and component termination. * Component termination and component body. Correct? Describe: * Coarseness / smoothness of the metal on the termination underneither the crack. * Solder left on the terminatio
Electronics Forum | Thu Jul 03 12:03:00 EDT 2003 | slthomas
So, there is a crack or gap between: * Solder and component termination. Bingo Correct? Describe: * Coarseness / smoothness of the metal on the termination underneither the crack. * Solder left on the termination. Unfortunately at 45X I can't rea
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Sat Sep 18 04:42:52 EDT 1999 | Brian
Dave, I'll respond by paragraph: | | | Brian: | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slathered shiitake burritos through