Electronics Forum | Mon Sep 09 18:10:35 EDT 2013 | davef
I don't know, but here is a link to a paper from the fine SMTnet Technical Library on a similar topic: http://www.smtnet.com/library/files/upload/Wire-Bonding-and-Soldering-on-Enepig.pdf Contact the authors and ask for their advice and help. BR, d
Electronics Forum | Thu Oct 05 07:23:34 EDT 2006 | Chris
Hi all experts, I have no background about PCB or SMT process. I am now encountering some issues after SMT - Unstable stitch bonding condition. I am now suspecting some contaminants remain on lead after cleaning. Therefore, how can I check th
Electronics Forum | Fri Oct 06 04:23:06 EDT 2006 | David
What is the solder finish of the board?. If this is gold, maybe you should check the reflow profile and max temperature which can easely kill your gold coating so problems with bonding. Also we are using Prozone Multicore with ultrasonic to clean
Electronics Forum | Thu Oct 05 16:04:00 EDT 2006 | GS
I am not expert, just my comment, the total ionic contamination allowed after SMT, by using No Clean process, theoretically it should be close to Zero. Any way the Standard IPC-JSTD-001 allows 1,56 ugr NaCl/cm2 for the final Printed Board assembled.
Electronics Forum | Fri Aug 17 01:40:55 EDT 2001 | V.RAMANAND KINI
We are in the watch & clock Business. We have a Watch IC chip that has to be wirebonded using Ultrasonic aluminium wedge bonder. The wire dia is 1.25mil. The PCB is made of G10 Glass epoxy copper clad laminate. The copper thickness is 18 microns. The
Electronics Forum | Fri Aug 17 11:55:31 EDT 2001 | davef
5uin. Your nickel thickness is fine. Although if you wanted to trade costs, consider giving-up nickel to 150uin thickness, while increasing the gold thickness. Gold over electroless nickel creates brittle joints because of phosphorous in the nicke
Electronics Forum | Tue Aug 21 22:24:36 EDT 2001 | davef
Root around here http://www.kns.com/resources/library/lib-wirebonding.asp
Electronics Forum | Mon Aug 27 15:06:29 EDT 2001 | davef
This otta push Wolfgang over the top ... Recommended reading G.G. Harman, Wire Bonding in Microelectronics : Materials, Processes, Reliability, and Yield, 2nd edition, McGraw-Hill Electronic Packaging and Interconnection Series, 1997. G.G. Harman, R
Electronics Forum | Tue Nov 07 22:44:39 EST 2017 | wrander1
Hi I'm new to the world of wire bonding. I seem to have some sort of pad contamination Preventing gold wire from bonding to aluminum pats. There appears to be a dozen microns size particles. And a slight crackling of the surface at 500 X. I am send
Electronics Forum | Wed Dec 14 12:34:56 EST 2016 | cy4223111
Hi all, Recently, we are trying to do wire bonding between a 75 * 75 um pad on a chip and substrate with 150 um height difference, but when completing wire bonding and the wire bonds on pad and substrate, the pad will get out of the chip easily