Electronics Forum | Fri Feb 22 15:16:24 EST 2002 | rkevin
Bet your using tin/ lead plated components with a lead free Cu/Ag/Sn alloy. It leads to intermetallic cracking. Wow didn't anyone tell you to check the archives yet, It seems to be the answer given to everyone. Why have an interactive site if you alw
Electronics Forum | Wed Sep 27 12:44:52 EDT 2000 | Ashok Dhawan
What could be possible resons for " Plating Crack on Barrel (tented via)" This tented via is in proximity to parts being hand soldered. The crack in barrel was detected on failure analysis - micro-section of via where barrel is having crack ( circul
Electronics Forum | Wed Jan 07 17:34:52 EST 2015 | duchoang
Customer puts our board to thermal test. Test cycle is -55c to 85c, repeat cycle in 15-20min. After 600 cycles, lot of TSOP joints are cracked, leads lifted. There are reasons such as thin PCB, mechanical impacts, warped PCB... My question is, how lo
Electronics Forum | Tue May 25 07:03:34 EDT 1999 | Milan Z.
After reflow proces in convection-IR oven we find broken body of SOT23 elements. There is no problems on other elements (SOIC, chip R,chip C, etc) Where is the problem? Thanks in advance!
Electronics Forum | Fri Jul 26 08:25:25 EDT 2013 | emeto
If there is a way to pre-tin the parts, that might help in forming better joint with gold.
Electronics Forum | Thu Jul 29 21:11:13 EDT 2004 | davef
Could be lots of things. With limited information about temperatures, solder alloy, and cleaning; we'll swing for the fence that you got these solder connections very hot. So hot that Pb oxide is dominating the solder joint surface instead of the
Electronics Forum | Fri Jul 26 05:14:38 EDT 2013 | anilw2006
We had a solder joint problem in gold plated PLCC68 ic. We do double sided reflow process with Cookson OL107F paste. First we do top with paste and second with glue process.The solder joint shape and wetting looked normal.In the process of testing
Electronics Forum | Thu May 26 21:09:01 EDT 2005 | thaqalain
The reliability of a Gullwing component solder joint is in question when insufficient solder is evident: *at the heel of the lead *at the toe of the lead *none of the above
Electronics Forum | Wed Jan 16 11:20:52 EST 2002 | bentzen
Hi... We tend to do a lot of footprint calculating for new SMD components. But what about the amount of solder paste on the solder pads. The amount of solder alloy is of cause determined by the stencil aperture size, stencil thickness and the sold