Electronics Forum | Wed Apr 14 19:47:13 EDT 2021 | solderingpro
Sounds like you may have already found the issue: inconsistency from your supplier. Seeing as Gold really doesnt oxidize and you're using an inert environment (N2 I suspect), I would turn my attention to the supplier. You said yourself, the "Shine
Electronics Forum | Wed Oct 27 19:50:59 EDT 1999 | chris
Hi What is the possible cause of non-wetting of solder paste to the gold land pad. What we observed in the surface of the non-wet pad is an organic FM, and using FTIR we found out that it is a flux. It is possible that the cause of non-wetting is
Electronics Forum | Tue Sep 01 11:30:28 EDT 2009 | rgduval
Is the solder wetting to the pad, and not to the part? If so, and all other things being true (same process, profile, solder), we'd suspect some contamination on the part preventing solder from wetting to the part. This could be tested by attemptin
Electronics Forum | Wed Oct 19 22:48:18 EDT 2016 | thaneshsivanadian
Hi All, Currently im seeing a cold solder/ poor wetting underneath the BGA Ball as i shown in the attachment. From the attachment you also can see one ball with poor wetting and another ball with a good wetting. When i checked with my re-flow profil
Electronics Forum | Tue Aug 11 14:09:30 EDT 1998 | Bucky Allen
Looking for Suppliers of surface mount wetting balance equipment.
Electronics Forum | Wed Jan 04 16:21:14 EST 2006 | jrlouden
What is the preferred method of under stencil wiping? (Wet or Dry wipe)
Electronics Forum | Mon Jul 28 05:35:17 EDT 2008 | surendra268
What could be the main reasons for De-wetting in reflow process. Can anybody answer
Electronics Forum | Thu Oct 28 09:25:35 EDT 1999 | Dave F
Chris: Typical non-wetting causes are: * Poorly controlled soldering process * Incorrect material * Surface contamination * Insufficient preheat * Misapplied solder mask * Shadowing Without intending to insult you, all of the causes of non-w
Electronics Forum | Thu Jan 25 12:18:40 EST 2007 | wagoner
There are several smd components in our factory that don't reliably wet to solder during reflow. Paste and placement are good, but the component won't wet reliably. All of the other components on the boards solder fine, but one of these components
Electronics Forum | Fri Nov 05 10:01:04 EST 1999 | Dave F
Chris: You can have more than "one question!!!" Anyhow, yes crappy solder paste can cause non-wetting, but before you go there understand why the paste is wetting some surfaces, but not others. Ta Dave F