Electronics Forum | Sat Dec 21 14:07:53 EST 2002 | No man land
cool Music soothens one's emotions. It should be > mild and not loud. No voice. Just > music...Solos. > > We have used this successfully > in our plant. Every hour we have a two minutes > break to give rest to our operators who use > microscope
Electronics Forum | Wed Jan 22 14:53:50 EST 2003 | MA/NY DDave
Hi I thought I would come back to this one for a second. Joe Fox above gave a nice concise note as to why you must raise the temp high enough above the soldering melting temp (liquidus) yet not too high. You want to go high enough for paste so tha
Electronics Forum | Thu Jan 23 20:27:54 EST 2003 | joeherz
Hello, We recently installed a new/used UPK 650 fitted with a foam fluxer using an RMA flux chemistry. We have had problems with icicling and bridging from the beginning. The bridging occurs mostly on DIPs and connectors. The icicling is on longer
Electronics Forum | Fri Mar 07 10:51:58 EST 2003 | MA/NY DDave
Hi O'Conner, I hope you also tell us what Universal-GeorgeW discusses with you. It is a little strange seeing his name on this list and his phone number. Gee I can give you his email address but won't.. Again distance engineering is tough. I woul
Electronics Forum | Tue May 27 12:40:50 EDT 2003 | davef
Hi Bill You said, "silicon". We assume by your discussion that you ment to say, "silicone". For background on silicone and soldering, check with Dow Corning [517-496-6000]. They make a OS2 [VOC-free] silicone stripper and should be able to give y
Electronics Forum | Tue Jun 10 16:51:19 EDT 2003 | davef
Develop your recipe wave soldering exactly as you developed your recipe for reflow soldering. The only difference is that instead of using your paste supplier's recommendations as the starting point, use your flux supplier's recommendations as a bas
Electronics Forum | Mon Jun 30 16:35:13 EDT 2003 | davef
Hi Steve We don�t double reflow this part. We wouldn�t consider it without a fixture or some other support. You know that sound, the almost involuntary sound that patrons in a restaurant make when a waiter drops a glass or a tray? It�s kind of an
Electronics Forum | Thu Jan 08 15:03:40 EST 2004 | dwzeek
We have an ongoing problem with our QFP144 packages soldering. It has not received much attention until late due to some customer failures. Most of the failures would show up in ESS testing and be repaired. The failure rate is about 2 in 1000 parts f
Electronics Forum | Tue Feb 03 06:52:45 EST 2004 | paul_bmc
About 2 years ago our company tried to go with a post reflow AOI inspection. This AOI was suppose to be able to inspect to a level class 3 product. **It is impossible** You cannot inspect for a heel fillet and inspecting for poor wetting is a very
Electronics Forum | Wed Apr 21 12:21:57 EDT 2004 | davef
Please help us understand your situation better. * How do �Having Problems W/ Parts Moving At Reflow� and �When the boards come out of the oven the pads look very wet from flux� relate to one another? * Tell us about solder, flux, reflow profile, and