Electronics Forum | Mon Apr 15 18:59:12 EDT 2002 | davef
Points are: * Seminal study is: "Evaluation of Low Residue Soldering for Military and Commercial Applications: A Report from the Low Residue Soldering Task Force," published by Sandia National Labs in June 1995. Look here http://www.smtnet.com/forums
Electronics Forum | Thu Dec 13 08:02:02 EST 2007 | realchunks
You may want to try raising your pre-heater if you have one. I would also suggest trying different fluxes that may be a little more active so you can use less. What type of fluxer are you using? Selective solder flux residue is a gray area. This i
Electronics Forum | Mon Mar 29 09:33:37 EST 1999 | Chrys Shea
| I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | What disadvantages are there when using this flux? | Do you have any contact details with
Electronics Forum | Tue Mar 30 08:11:27 EST 1999 | George Steele
| | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | What disadvantages are there when using this flux? | | Do you have any contact detail
Electronics Forum | Mon Apr 05 08:25:31 EDT 1999 | ADRIANO FERNANDES
| | | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | | What disadvantages are there when using this flux? | | | Do you have any contact
Electronics Forum | Mon Feb 05 09:42:21 EST 2007 | George
Hello everybody, What is considered "high frequency" when we talk about possible issues with NO-clean flux residues and product's application? I appreciate your help on this... Have a good one! George
Electronics Forum | Mon Jan 27 12:02:00 EST 2003 | Mike Konrad
Dave is correct. No-clean flux + water = white residue (unless the proper chemical is mixed with the water). Additionally, no-clean flux + IPA = white residue. Many saponifiers work well as do other cleaning agents. White residue may also be a re
Electronics Forum | Tue Sep 21 13:10:10 EDT 1999 | Dave F
| Dear All, | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | I mean that I wonder why we use
Electronics Forum | Fri Dec 16 11:21:18 EST 2005 | patrickbruneel
Steve, Water-soluble fluxes are per definition very corrosive and need to be cleaned (read the data sheet) Encapsulation will prevent humidity reaching the water-soluble acids but will not prevent reducing the metals the flux is in contact with to m
Electronics Forum | Wed Aug 10 17:19:24 EDT 2005 | Steve Stach
The propensity for flux residues to cause shorts can be increased in humid environments where water molecules hydrate the surfaces. At high frequencies, electrons travel on the surface of conductors/insulators, increasing the likelihood of shorts in