Electronics Forum | Mon Sep 21 08:14:14 EDT 1998 | Steve Gregory
| Hello: | I would like to know what causes tombstombing and how can it be prevented? | Thx. | Nichol Hi Nichol! A tombstone happens when solder doesn't wet equally on both terminations during reflow...now why that happens can be found by looking at
Electronics Forum | Mon Sep 14 11:56:38 EDT 1998 | Ben Salisbury
| Our company currently donesn't have any type of sonic wash to wash boards that have been "miss printed" Wanting to know the best way to go about this. So what we are having to do is spray down the boards with alcohol and wipeing the solder paste
Electronics Forum | Tue Aug 18 16:10:40 EDT 1998 | Earl Moon
| Question: | If a PCB and the lands of a part both had electroless plating, would there be a higher tendancy for intermetallics to form in and on the solderjoint...versus just the PCB or Just the part being plated? | I'm currently running into this
Electronics Forum | Thu Aug 13 12:55:46 EDT 1998 | Dave F
| Hi, can you please tell me how to make green coating and through-hole plating of PCB? Thanks! | Xingsheng Xingsheng: Welcome. Bible on PCB fabrication: Printed Circuits Handbook, Clyde Coombs, McGraw-Hill Web resources: http://www.pwbrc.org/ a
Electronics Forum | Fri Jul 10 09:56:11 EDT 1998 | Justin Medernach
| I am looking for some guidelines on evaluating solder paste. I am specifically interested in No-Clean Pastes, as they are a completely new ball game when it comes to slump, tack time, stencil life, tack time, etc. | Thanks for any and all help give
Electronics Forum | Thu Jul 09 11:32:16 EDT 1998 | Justin Medernach
| What should a good gold joint look like? We've run boards for our customers that look kinda dull but seemed to wet properly and the boards fired up just nicely! Should they look nice and shiny like our HASL boards or is "a shiny joint is a good joi
Electronics Forum | Thu Jul 02 14:46:34 EDT 1998 | Steve Schrader
| I'm having a problem getting good reflow on gold sufaced boards. The profile looks good and I have adjusted it both hotter and colder and adjusted the various times ( soak, reflow ) to no avail. What realy gets me Is that a month ago we built some
Electronics Forum | Fri Jun 26 16:23:14 EDT 1998 | Steve Gregory
Hi Dave! Yeah, they've been around a while, and they're pretty straight foward like you said. About the only things that I can think of that I've run across that causes problems with these guys is when they're used on the bottomside of the board
Electronics Forum | Thu Jun 25 15:33:51 EDT 1998 | Earl Moon
| | Hi there, | | Does any one know what is TCE for fully wet saturated FR4. I came to know that for Dry FR4 the TCE is about 15-19 PPM �C. Is that true? | | | | Appreciated for your help. | | rgs, | | chiakl | Chiakl, | It looks like you are speaki
Electronics Forum | Wed Jun 24 07:32:40 EDT 1998 | Brian Conner
| | I am experiencing a wave-soldering problem with a leaded capacitor - too much solder above the board!! The capacitor lead is .020" dia. and the hole size is .038". This only occurs on the negative lead of the component. The capacitor is also a