Electronics Forum | Thu Sep 09 22:18:13 EDT 1999 | Dave F
2 will have enormous impact on every other process. | | | thank in advance. | | | scott. | I appreciate your sincere answer. | would tell me the hint about printer if i's possible | To tune our smt process we have to know what is the major X
Electronics Forum | Wed Aug 25 15:51:58 EDT 1999 | JohnW
| Does anyone have any information on stencil aperture/pad ratios for noclean solder paste. In the past I have experienced severe solder ball problems when using the same size apertures from aqueous products as I do with the No-clean products. Cons
Electronics Forum | Sat Aug 21 12:29:28 EDT 1999 | Brian
| I have a layer of electroplated solder (10/90) that appeares to have some sort of contaminent on it. Water will not wet to the layer in some areas. I have tried using 10% HCl in DI as a cleaner as well as 7.5% Fluoboric acid in DI. Neither has t
Electronics Forum | Wed Aug 18 11:52:35 EDT 1999 | Brian
| WE ARE CURRENTLY HAVING PROBLEMS REFLOWING BOARDS WITH WHITE TIN PLATING. WE ARE NOT GETTING GOOD WETTING ON THE PADS. | WE HAVE CHECKED THE REFLOW PROFILE AND TRIED DIFFERENT PASTE'S. | WE THINK THERE MAY BE CONTAMINATION OR OXIDATION ON THE PADS.
Electronics Forum | Thu Jul 15 19:05:58 EDT 1999 | Earl Moon
| | | We have been encountering diminishing ball shear readings these past few weeks, despite the fact that we did not change any ball shear tester parameter. Our reflow parameters are also within spec limits. ( 210-220 deg C max temp. and 40-60 sec
Electronics Forum | Mon Jun 28 15:50:22 EDT 1999 | JohnW
Hey there gang, how's it going ? Anyway's here's my probelm, got a new product to build double sided reflow, lot's of so20's and PLcc's 1206's, 0805's the usual stuff. Probelm is all the pad spacing of the 1206's are too big, my component's are only
Electronics Forum | Mon Jun 28 16:18:44 EDT 1999 | Earl Moon
| Hey there gang, how's it going ? | | Anyway's here's my probelm, got a new product to build double sided reflow, lot's of so20's and PLcc's 1206's, 0805's the usual stuff. Probelm is all the pad spacing of the 1206's are too big, my component's ar
Electronics Forum | Mon Jun 28 17:03:59 EDT 1999 | M Cox
| Hey there gang, how's it going ? | | Anyway's here's my probelm, got a new product to build double sided reflow, lot's of so20's and PLcc's 1206's, 0805's the usual stuff. Probelm is all the pad spacing of the 1206's are too big, my component's ar
Electronics Forum | Fri Jun 18 20:09:52 EDT 1999 | Dean
| Has there anyone bold enough to try this in their shops? My cubemate just got through telling me that at his last shop, they had bare copper boards (no HASL, no OSP, no nothing), with minimal solderability problems. | yes, 8 years ago I developed
Electronics Forum | Thu Jun 03 20:09:56 EDT 1999 | C.K.
I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole." These def