Electronics Forum | Wed Oct 10 13:51:08 EDT 2007 | petep
Coilcraft has posted the following and I am wondering how you folks are handling the use of coils in a Water Soluble world. PCB Washing and Coilcraft Parts Coilcraft tests for resistance to solvents per the following specification: Resistance to s
Electronics Forum | Mon Feb 25 08:10:47 EST 2002 | jax
Eric, I assume you are talking about "VOC" as in (MXL-350VC "VOC FREE" Swing Spray Fluxer) since I have never heard of "VCO" used when talking about Spray Fluxers', or anything else for that matter. This is copied right from the SMTnet Library: VOC.
Electronics Forum | Thu Jul 13 10:10:48 EDT 2000 | Todd
Donnie In response to your questions; 1. Flux is Multi-core X32-10M 2. Preheaters temperatures can range based on board density. the goal is to get the top side to 100C before wave. 3. Components can't be placed after wave solder, they are surface m
Electronics Forum | Fri Nov 05 17:29:53 EST 2004 | Steve Stach
Most metal stencils today are cleaned with a water based cleaning solution. 3 choices are most typical: (1) Water only for water-soluble paste (2) Water + Organic for rosin and no-clean (low residues. This affords lower temperatures and is easier t
Electronics Forum | Tue Feb 28 14:32:26 EST 2006 | masrimhd
As I know, the encapsulation effect occurs only with rosin based fluxes. So if you have a PBA soldered using RA Flux, you should either wash it well, or leave it alone and it will be safe. For NC process the story is different because there�s no re
Electronics Forum | Wed Apr 27 10:52:52 EDT 2005 | saragorcos
Have you examined what type of residue is present? It is possible that what you are seeing is benign, though flux that is not fully activated often leaves harmful residue species such as chloride or weak organic acids. If you don't want to change p
Electronics Forum | Tue Jun 29 13:52:32 EDT 2004 | microniks
Where to find detailed information on fluxes? No one seems to know the real difference between Rosin fluxes with colophan, Resin fluxes or synthetic Resin fluxes, No Clean, Low Residues, VOC-Free, Halide-Free, Water Washable with alcohol base, Resin-
Electronics Forum | Tue Jun 29 13:56:27 EDT 2004 | Pierre
Where to find detailed information on fluxes? No one seems to know the real difference between Rosin fluxes with colophan, Resin fluxes or synthetic Resin fluxes, No Clean, Low Residues, VOC-Free, Halide-Free, Water Washable with alcohol base, Resin-
Electronics Forum | Wed Aug 10 08:10:39 EDT 2005 | davef
Comments are: * Sounds like it's necessary to clean "heareous F381, F352 no clean solder paste" in your application. Consider a paste that may be better suited to your application. * If you're cleaning "low residue flux", consider using an organic ac
Electronics Forum | Tue Jul 10 19:16:08 EDT 2007 | 5why
We have filed returned (approx. 5%) of the boards that exhibit inner layer short @ a particular connector locations. X-section revealed there exhibit Cu residue, but aside from that, we also suspect there could be organic contaminant, what test shou