Electronics Forum | Fri Dec 13 12:12:21 EST 2002 | Hank Sybesma
We are being asked to begin rework processes on boards that use lead free solder. Does anyone have any experience in the service field working with lead free?
Electronics Forum | Tue Nov 24 18:54:36 EST 2009 | gregoryyork
Some companies claimed their lead free solders wouldnt attack stainless steel, frankly they do and they should not be allowed to get away with these claims. Lead Free does not attack Cast iron
Electronics Forum | Wed Feb 15 01:49:34 EST 2017 | soldertraining
Hi I completely agree with you. Also, the Dry Solder paste can be used in wireless repair operations such as the repair of smart phones, tablets, laptops and other handheld devices. The lead-free solder paste can be squeegeed through the apertures of
Electronics Forum | Wed Jun 29 17:35:46 EDT 2005 | Hiram
Hi all, Does anybody have any comments on the lead-free alloy SN100C from AIM solder? I am in the process of selecting the "right alloy" for our lead-free wave solder machine. We manufacture A/V equipment. I appreciate your feedback as usual. Hir
Electronics Forum | Thu Oct 01 09:58:30 EDT 1998 | Jacqueline Coia
Could you tell me please when the lead free solder regulation will become mandatory in Europe and also what are the current industrial alternatives for paste, bar and wire. Cheers, Jack
Electronics Forum | Thu Jun 30 13:42:55 EDT 2005 | Hiram
Thank you all for the information... Hiram
Electronics Forum | Wed Apr 14 20:24:48 EDT 2004 | Ken
What do you mean the solder must "survive" 260C? What is your target temperature? Is it dictated by a component, the substrate or the solder alloy? Do you require a eutectic alloy? If not, the selection of alloys grows. (these are from memory...n
Electronics Forum | Mon Sep 29 10:04:40 EDT 2008 | illheader
Has anyone used lead free 99C bar solder/paste? Looking for more information other than what the manufacturers give you. Thanks
Electronics Forum | Thu Jul 28 09:47:06 EDT 2005 | fctassembly
Hello Carl, The main reason there is little information on lead free soldering to ENIG is because most of the lead free soldering to date has been Japanese consumer products. To keep costs down, the major surface coating used has been OSP copper. It
Electronics Forum | Mon Jun 23 11:24:12 EDT 2003 | procon
Titanium components are best for any suface in contact with lead free solder. We will be offering our brand solder fountain rework station utilizing Titanium components in July. Lead-Free solders seem to adhere to SST or cast pots and cause blockages