Electronics Forum | Tue May 09 14:23:40 EDT 2006 | flipit
I would like to know what you are seeing in production. I have read the papers that state fewer tombstones with SAC305 as well as the papers that state more tombstones with SAC305. I am seeing more tombstones with SAC305. I place a lot of 0402 com
Electronics Forum | Tue Oct 05 12:46:02 EDT 2021 | emeto
From what I understand SAC305 and SAC405 are considered low silver content and have the better overall mechanical qualities compared to more silver or no silver.
Electronics Forum | Fri Oct 01 01:25:55 EDT 2021 | sn
Thank you Djo for your sharing. By the way, do you know that which field/product will prefer to use SAC405 paste instead of SAC305 or lower Ag wt% alloy solder paste?
Electronics Forum | Thu May 25 12:28:56 EDT 2006 | inds
no there is lot of difference between both the alloys.. SN100C works better than SAC305... gives little more time to remove and replace the unit without completely loosing the Cu... but there are customers who still prefer sticking to SAC305... so th
Electronics Forum | Mon Jan 02 08:54:58 EST 2006 | aj
has anyone used or trialed the SACX from Alpha, from reportes and studies carried out it seems that its a go between SAC305 and SN100.
Electronics Forum | Thu Apr 06 17:42:59 EDT 2006 | GS
found this interesting comparison (SAC305 SN100C) http://www.nihonsuperior.co.jp/english/data/pdf/nse2_1.pdf Regards..........GS
Electronics Forum | Fri May 19 13:40:36 EDT 2006 | grantp
Hi, Sorry to drag this thread up again, but we were recommended to change the wave to SAC305, but is everyone recommending SN100C? That seems to be the feeling on this thread. What flux is used? Regards, Grant
Electronics Forum | Tue Aug 22 09:57:15 EDT 2006 | picman
I must prepare formal report abaut comparison of the SM988 and SAC 305 wave soldering( as a .ppt file). May you help me please ?
Electronics Forum | Fri May 05 08:23:07 EDT 2006 | molosse21
Hi everyone We plan to use on our smt line sac 305 and on our wave soldering sn100c. Will there be a compatibility problem if we do make touch up with sn100c on smt or touch up thru hole components with sac 305 ??? Thanks for taking time to reply