Electronics Forum | Sun Jan 31 22:55:33 EST 1999 | Dennis O'Donnell
| | Hello Netters, | | | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI
Electronics Forum | Wed Feb 03 04:44:43 EST 1999 | Jeff Sanchez
| | | Hello Netters, | | | | | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that t
Electronics Forum | Mon Mar 01 22:24:53 EST 1999 | Dave F
| It seems to be that we have to much NaCl left on our assambled PCB's. | The flux we use is from cobar. They say it can not be from the flux... So what can be the reason, what kind of problem may occer when there is to much NaCl. | George: When so
Electronics Forum | Wed Jun 27 21:17:37 EDT 2001 | davef
;-) Earth to Genny: Hellooooow!!! No one knows the answer. We�re guessing that it might not be a problem, but we don�t know!!! We are not holding-out to drill you. We�d tell you, if we knew, honest. ;-) The people that are goofy enough to do
Electronics Forum | Thu Oct 02 21:00:26 EDT 2003 | davef
Who says the chlorine comes from your tap water? Our PTOW dumps boat loads of chlorine into our water periodically. Sometimes it's so bad you can smell it. We doubt that it is the source of your problem. This chlorine will volitize very quickly,
Electronics Forum | Thu Aug 05 06:29:18 EDT 1999 | Graham Naisbitt
| | | We're getting field failures in a high impedance portion of the circuit. Think the unpopulated pc card has contaminates because we were able to grow dendrites by applying a 9 volt battery across the suspected pad, placed a drop of de-ionized w
Electronics Forum | Sun Jan 31 03:28:24 EST 1999 | Jeff Sanchez
| Hello Netters, | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI solde
Electronics Forum | Tue Jul 28 16:13:45 EDT 1998 | Steve Gregory
| Hello everybody. | Remember I posted some questions on the smtnet regarding placing the thru hole connector using paste and reflow(pin in hole). I have able to accomplish the process succcesfully.....but I have a problem. The boards are failing at
Electronics Forum | Fri Jul 10 09:56:11 EDT 1998 | Justin Medernach
| I am looking for some guidelines on evaluating solder paste. I am specifically interested in No-Clean Pastes, as they are a completely new ball game when it comes to slump, tack time, stencil life, tack time, etc. | Thanks for any and all help give
Electronics Forum | Wed Dec 19 01:17:13 EST 2001 | ianchan
Hi Experts, I need help here, advice appreciated from all... Production is running a Lot of flex-circuit PCB, through the SMT line, with 0402 components. The flex-PCB is taped to FR4 support "pallets" when processing thru' the SMT P&P m/c. We use