Electronics Forum | Tue Dec 27 04:07:56 EST 2016 | anhsang38
Dear Pro, Pls, increase temperature up to 255ºC and considering solder's profile. Good luck
Electronics Forum | Tue Dec 27 18:29:57 EST 2016 | anhsang38
Dear pro, Could you show the solder's profile.
Electronics Forum | Thu Dec 29 10:39:19 EST 2016 | luciano
Thanks Anshang38 I'll try and get a profiler.
Electronics Forum | Thu Dec 29 10:41:42 EST 2016 | luciano
Thanks Evtimov, The flux is brand new and the amount of flux is enough and consistent across the surface of the boards.
Electronics Forum | Wed Dec 28 20:56:14 EST 2016 | anhsang38
Dear Pro, Pls, try to get solder's profile from solder supplier. That is the most important in wave soldering process... if not you will be difficult for improvement. Good luck.
Electronics Forum | Tue Dec 27 15:07:28 EST 2016 | luciano
Hello, Sorry for the mistake. The speed is 1m/min. We are using Alpha Vaculoy solder and a conveyor angle about 7º. We are not using pallets since the fingers hold the boards directly. Thanks!
Electronics Forum | Thu Dec 29 10:07:14 EST 2016 | emeto
Luciano, It looks you have no flux there. Please flux one board by hand and send it through the wave. That will eliminate a lot of the possibilities.
Electronics Forum | Tue Dec 27 10:18:03 EST 2016 | anhsang38
Dear Pro, I want to confirm with you about conveyor speed. is 1m/s? We are using wave soldering but it is 1.2m/min, min not second. Pls, check it agian. The flux is not relative this error. It is relative no sodering, bridge. The solder bar is the
Electronics Forum | Tue Dec 27 06:52:34 EST 2016 | luciano
Thanks for your advice. I've tried setting the temperature up and even measuring the temperature at the wave itself but had no luck at all. I've also tried using temperatures going from 245 ºC up to 260 ºC. The amount of flux was adjusted as well a
Electronics Forum | Thu Dec 29 10:47:22 EST 2016 | luciano
Thanks SuMoTe, I've already tried fluxing various boards (new clean ones and older ones) without turning the waves on and with different temperature setups (within the suggested params from Alpha) in the preheat zone. The results were in many cases