Electronics Forum | Wed Jul 03 03:02:35 EDT 2013 | autoel
How to test the reflow solder joint shear strength? What are the specification to test solder joint shear strength? What are the different methods to test the solder joint shear strength? Vijayashree
Electronics Forum | Wed Jul 03 15:40:17 EDT 2013 | davef
Shear tests are [in my opinion] senseless. The shear stress you measure depends more on the shear rate and on the point where the force is applied than on the grain structure. When shearing a component, you not only apply shear stress, but also roll
Electronics Forum | Wed Nov 26 11:19:58 EST 2008 | vladig
I don't think you can find any specs on that. As long as a solder joint can not be broken by virtually "blowing over it" any reading on the UTS, or shear strength can be very confusing. You can specify, though that the assembly (joint) should withsta
Electronics Forum | Wed Mar 30 16:07:24 EST 2005 | Dreamsniper
If there's no shear strength standard for solder joint, how will I define my pad width and length then. I have a 8.5 mils width and my component lead width is 8.66 mils based on manufacturer's minimum width specification. How will I identify that it
Electronics Forum | Wed Mar 30 16:46:03 EST 2005 | chunks
There is no spec because solder is designed to provide an electrical connection not a mechanical connection to hold the part on. If it where mechanical we�d be welding our parts on. Your pad width and length are derived from your component manufact
Electronics Forum | Wed Oct 06 22:55:14 EDT 2004 | davef
Your customer is correct. Components should not fall a board during a reasonable drop test. A shear test poorly represents a drop test. A drop test represents a drop test very well. If you want to proceed with shear testing, search the fine SMTne
Electronics Forum | Tue Mar 22 07:39:05 EST 2005 | davef
There is no standard. This is a relative test. If you wish to do tests of this kind, we suggest to pay attention to the following points: * Shear strength of soft solder depends on the deformation speed applied. The faster the material is deformed t
Electronics Forum | Fri Mar 30 20:06:55 EST 2001 | aortiz
Maybe there's no test and I don't know where or why my customer came with that requirement (I think because in one of the board shipments he got a board were a smd resistor broke, but I think that happened because miss handling), but anyway I need so
Electronics Forum | Wed Oct 06 03:18:01 EDT 2004 | Joseph
Dear all, Recently our customer complaint that some components being came off from the pcba after dropping test.But the curious is, the leads show visible solder fillet covering more than 75% of termination area on pad, which is acceptable as per IP
Electronics Forum | Fri Mar 30 13:06:50 EST 2001 | aortiz
Hi, I need support on the method or applicable standard to measure the shear force strength on chip capacitors and resistors. I know the soldered joints strength is related to land desing, solder volume, pcb and component solderability, component