Electronics Forum | Fri Nov 25 20:57:30 EST 2016 | sarason
You guessed right. Not hot enough to get good reflow. regards sarason
Electronics Forum | Fri Nov 25 05:16:44 EST 2016 | slavek
Hello, I want to ask on suitable temperature profile for PCBs with ENIG final surface finish. I know that it is complex question with many unknowns. When the PCB will be standard 1,5 mm 35/35 Cu and the amount of components will have any influence o
Electronics Forum | Sat Nov 26 00:56:17 EST 2016 | slavek
thank you sarason
Electronics Forum | Fri Sep 21 11:02:37 EDT 2001 | davef
You can measure temperatures any place that you would like, but the issue is the temperature of the solder. We've seen solder temperatures that vary from lead to lead on the same component. Why don't you want to measure the temperature of your so
Electronics Forum | Fri Sep 21 10:44:34 EDT 2001 | slthomas
You can, and for small parts you probably won't see much difference between body temp. and lead temp. For QFPs or PLCCs there will be a much greater delta, though. I'd be more concerned with the small surface area you're making contact on (spherica
Electronics Forum | Tue Feb 13 15:56:16 EST 2007 | darby
Campos, This is a direct reply I recieved from Indium, (thanks to Rich Brooks), in late 2004 regarding SMQ230. I have followed these guidelines with good results using ENIG finish. Same also applies to Indium 5.1 apply to both alloys (SAC 387 and 305
Electronics Forum | Wed Sep 15 10:55:21 EDT 1999 | Scott S. Snider
| Hi, | | Can someone pls suggest to me the best reflow temperature setting | for a force air convection oven. The details is as follow. | 1) Heller 1700s | 2) 12 zone---6 top and 6 bot | 3) Solder paste --- Qualitek 691 non clean | 4) board size :
Electronics Forum | Wed Sep 15 07:43:12 EDT 1999 | Earl Moon
| Hi, | | Can someone pls suggest to me the best reflow temperature setting | for a force air convection oven. The details is as follow. | 1) Heller 1700s | 2) 12 zone---6 top and 6 bot | 3) Solder paste --- Qualitek 691 non clean | 4) board size :
Electronics Forum | Thu Apr 05 12:27:12 EDT 2001 | davef
I concur with your second approach. A profile needs to be tailored to the design of the board, the components, and the solder paste. Your first approach seems to try to balance lower quality soldering with a lower process complexity.
Electronics Forum | Wed Sep 15 12:07:50 EDT 1999 | Earl Moon
| | Hi, | | | | Can someone pls suggest to me the best reflow temperature setting | | for a force air convection oven. The details is as follow. | | 1) Heller 1700s | | 2) 12 zone---6 top and 6 bot | | 3) Solder paste --- Qualitek 691 non clean | |