Electronics Forum | Thu Feb 17 15:01:23 EST 2005 | davef
We're not familiar with your DYMAX #984-LVUF. The problem is not with your conformal coating. The problem is with your 0805 [and not all of 0805, probably just those from a specific supplier]. This lack of coverage of components is called dewetting
Electronics Forum | Tue Sep 21 16:09:08 EDT 2004 | davef
Q1: What is "enough surface free energy"? A1: Look here for background: http://www.azom.com/details.asp?ArticleID=1575 Q2: How do I determine surface free energy? A2: We look at it a relative term. For instance, a semi matte finish on solder mask
Electronics Forum | Fri Sep 07 09:55:19 EDT 2007 | russ
what type of solder paste are you using? Why the concern over wetting spread to the edge of pads? Are the solderjoints formed correctly at the component? Russ
Electronics Forum | Thu Jul 09 11:13:00 EDT 1998 | justin medernach
| IS IT BETTER FOR SOLDER PASTE TO SPREAD OUT AS FAR AS POSSIBLE ON BARE COPPER, OR FOR IT TO KEEP THE SHAPE OF THE PRINT? I'VE BEEN DOING SOME SOLDER PASTE EVALUATIONS, AND I'M TRYING TO EVALUATE THE RESULTS. I'M NOT SURE THAT BECAUSE A PASTE MAY
Electronics Forum | Thu Sep 06 22:01:21 EDT 2007 | syedsmt
Hi! I am Syed from Hitachi located in Malaysia.It seems that the discussion about OSP is very much related to the dillema that I am facing in my company.I am the Senior Executive for the SMT Department at Hitachi.Currently we are facing some issues w
Electronics Forum | Tue Aug 24 15:30:51 EDT 1999 | John Thorup
| | This is out of the normal scope of this site but� | | | | I am in search of a Digital Camera for use with documentation instructions. What would be the Minimum Resolution that I should require? I will need details of assemblies such as Compone
Electronics Forum | Thu Mar 08 08:03:16 EST 2007 | ck_the_flip
ENig can vary in quality, but I've never seen an ENiG board that's been downright unsolderable. At a CM where I worked, I had to prove a QE wrong. He was flippin' out (*no offense*) about black pad, something commonly seen on ENig boards, so what I
Electronics Forum | Mon Oct 16 20:29:32 EDT 2000 | Dave F
Jason: How did you determine that the deposits are tin oxide? What does this stuff look like? Klein Wassink "Soldering in Electronics" (p. 221, quoting original work by others). States (in effect) tin (or solder) quickly forms a protective oxide
Electronics Forum | Tue Sep 21 10:53:53 EDT 2004 | davef
We know nothing about Envivar UV 1244 and you weren't real clear about the details of the problem or the materials [eg, ws flux, solder mask, etc], but we'd speculate your adhesion problem goes back to the cleanliness of your board. First by 'alcoho
Electronics Forum | Wed Sep 07 16:53:15 EDT 2005 | GS
Contact Cookson Electronic, they can support you with OSP solutions (ENTEK---) new formulations for Lead Free apllication. Regards GS --------- from a 2003 Cookson presentation: Objective Although Existing ENTEK� PLUS CU106A technology is suc