Electronics Forum | Fri Feb 20 12:55:43 EST 2004 | russ
Ah, the old contour wave. I don't really know how to adjust those to get correct backflow to reduce your solder volume. I need to ask why you are worried about this. Do you have a QC requirement in excess of IPC class3 wich allows for this joint t
Electronics Forum | Thu Feb 19 09:02:43 EST 2004 | russ
This is a pretty common sympton when wave soldering chip components. As a note IPC allows for this in wave process. The problem is in the pell off of the wave and you may not be able to fix. Is your back flow off of the wave only present when a bo
Electronics Forum | Thu Feb 19 18:07:57 EST 2004 | davef
We're inclined to buy Russ's stuff about peel from the wave. Look here, but shield your eyes first: [ http://www.thepdfshop.co.uk/ppm/defects/Wave/asp/50.asp ] [A respectful bow to BW for the pix] Could you tell us more about: * Board direction thro
Electronics Forum | Wed Nov 26 11:19:58 EST 2008 | vladig
I don't think you can find any specs on that. As long as a solder joint can not be broken by virtually "blowing over it" any reading on the UTS, or shear strength can be very confusing. You can specify, though that the assembly (joint) should withsta
Electronics Forum | Thu Feb 19 13:43:01 EST 2004 | northern
What would cause this? Too much pre-heat, not enough, too much dwell, not enough? I am staying within the flux specs for preheat and can't seem to affect it much. Can board/parts contamination lead to this? I think that is a reach but I'm runnin out
Electronics Forum | Wed Nov 26 09:16:59 EST 2008 | barryg
Hello everyone, after a short layoff I am glad to be back. I have a question. I have a button (snap button) that is being soldered to a strip of sac coated copper. We are questioning the joint strength of this from our vendor as we see these popping
Electronics Forum | Mon Feb 23 20:19:15 EST 2004 | greg york
Has anyone ever seen a bulbous joint (on 1 side > of 1 designator) on every board? I checked the > preheat profile at the wave and have played with > dwell times but can't get rid of it. I checked > the archives and didn't find much. Any help wou
Electronics Forum | Thu Jun 19 10:47:29 EDT 2003 | Eric QE
Caltex or Ersa type system is good, Caltex prisms, necessary for looking underneath the BGA can be crashed easily when looking under low profile or Micros. $40-$110 each depending on the availability and who makes 'em. We have 2D and 3D X-ray avai
Electronics Forum | Wed Jul 03 03:02:35 EDT 2013 | autoel
How to test the reflow solder joint shear strength? What are the specification to test solder joint shear strength? What are the different methods to test the solder joint shear strength? Vijayashree
Electronics Forum | Tue May 27 11:59:14 EDT 2003 | blnorman
Is anyone aware of any reports, studies, articles on the subject of silicon contamination in SnPb solder joints. We are evaluating repair of conformally coated (silicone) boards. The fear is that we will never totally remove the silicone and once i
Our Company handle AOI (Auto Optical Inspection) and SPI (Solder Paste Inspection) Machines.
Equipment Dealer / Broker / Auctions
Hwaseong-si, Gyeonggi-do, Korea
Hwaseong-si, South Korea
Phone: +82-1029254936