Effects of Package Warpage on Head-in-Pillow Defect
Published: |
July 6, 2017 |
Author: |
Zhenyu Zhao1, Chuan Chen, Yuming Wang, Lei Liu, Guisheng Zou, Jian Cai and Qian Wang - Tsinghua University, Chang Yong Park - Samsung Electronics |
Abstract: |
Head-in-pillow (HiP) is a BGA defect which happens when solder balls and paste can't contact well during reflow soldering. Package warpage was one of the major reasons for HiP formation. In this paper, package warpage was measured and simulated. It was found that the package warpage was sensitive to the thickness of inside chips. A FEM method considering viscoelastic property of mold compound was introduced to simulate package warpage. The CTE mismatch was found contributes to more than 90% of the package warpage value when reflowing at the peak temperature. A method was introduced to measure the warpage threshold, which is the smallest warpage value that may lead to HiP. The results in different atmospheres showed that the warpage threshold was 50μm larger in N2 than that in air, suggesting that under N2 atmosphere the process window for HiP defects was larger than that under air, which agreed with the experiments.... |
You must be a registered user to talk back to us. |
Company Information:
More SMT / PCB assembly technical articles »
- Mar 19, 2024 - What is Underfill | GPD Global
- Mar 19, 2024 - Made in Japan: Solder Paste Jet Dispensing Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 26, 2024 - Precision Control in Electronic Assembly: Selective Wave Soldering Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 02, 2024 - Maximizing Efficiency: The High-Speed SMT Line With Laser Depanelizer | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Dec 27, 2023 - Revolutionizing Tech: SMT Auto IC Programming Machine Mastery | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Browse Technical Library »
Effects of Package Warpage on Head-in-Pillow Defect article has been viewed 894 times