Electronics Forum | Thu Dec 24 08:44:25 EST 1998 | Earl Moon
| | | | Folk's, | | | | I'm in need of some help / direction. I'm working on my thesis for a masters based on looking at the effect's of the solder resist promoting / reducing the amount of solder ball's during wave. I'm looking at thing's like colou
Electronics Forum | Mon Jul 17 13:37:35 EDT 2006 | carln
Here is something I copied from Circuitnet.com. This appears to answer your question and then some... http://www.circuitnet.com/experts/ Ask the Experts Jul 17, 2006 What type of cleaner method is preferred for lead-free stencils? What type of s
Electronics Forum | Fri Mar 21 15:51:23 EDT 2008 | g2garyg2
Thought I would reply and try to assist. PROMATION, my company, also manufactures Diode Laser soldering systems but with this stated we also manufacturer iron tip systems, soft beam systems and hot air solutions. The reasons are simple. Diode Laser
Electronics Forum | Wed Oct 03 23:58:23 EDT 2018 | gaintstar
Flason SMT News: http://www.flason-smt.com/new/6-Things-to-Check-Before-Submitting-Your-PCB-Design-for-Manufacturing.html http://www.flason-smt.com/new/about-wave-soldering-machine-tin-pot.html http://www.flason-smt.com/new/Advantages-of-Design-for-
Electronics Forum | Thu Jun 03 10:09:59 EDT 1999 | Earl Moon
| In a month or so, we will be getting an in-line x-ray inspection machine. It will require that we solder our most comlicated side (normally top) first. This is opposite to our process now where we solder our passive (bottom) side first. We cann
Electronics Forum | Thu Jun 03 14:06:16 EDT 1999 | Dave F
| | In a month or so, we will be getting an in-line x-ray inspection machine. It will require that we solder our most comlicated side (normally top) first. This is opposite to our process now where we solder our passive (bottom) side first. We ca
Electronics Forum | Thu Jun 03 15:19:14 EDT 1999 | Earl Moon
| | | In a month or so, we will be getting an in-line x-ray inspection machine. It will require that we solder our most comlicated side (normally top) first. This is opposite to our process now where we solder our passive (bottom) side first. We
Electronics Forum | Tue May 18 16:22:43 EDT 1999 | Earl Moon
| | | Hi Guys, | | | | | | I am going to be graced with the good luck of processing microBGA's in the near future. A bit of a step forward from printing 20-mil pitch and wave soldering 0805's, wouldn't you say? | | | | | | So, any of you folks who
Electronics Forum | Sun Nov 08 15:27:25 EST 2015 | davef
Thinner: Flux thinner, NOT paint thinner We kept a spare stone in thinner in inventory. We cut PVC pipe to size, cap in one end, screw thread on the other, stone inside, filled with flux thinner and covered with a screw cap. I don't remember who we
Electronics Forum | Wed Sep 20 17:06:23 EDT 2000 | jackofalltrades
On the Vitronics/Soltec Wave Soldering Machines, we have no problems with the hot air knife (called a "Select X De-Bridging Tool" by Vitronics). We have both Delta's and Delta Max's. We have used both air and nitrogen with no problems. When using a "