Electronics Forum | Thu Oct 15 16:41:28 EDT 1998 | Dave F
| | All Y'll | | | | How do you clean components that must be added to an assembled board after water wash? | | | | BACKGROUND | | | | Our basic process goes like this: | | | | 1 Print paste with OA flux, place, reflow, wash | | 2 Repeat 1 | |
Electronics Forum | Sat Oct 17 10:50:11 EDT 1998 | mike
| | | All Y'll | | | | | | How do you clean components that must be added to an assembled board after water wash? | | | | | | BACKGROUND | | | | | | Our basic process goes like this: | | | | | | 1 Print paste with OA flux, place, reflow, wash |
Electronics Forum | Tue Sep 21 11:39:41 EDT 2004 | pabloquintana
Conformal coat a bare board to determine if there > is there is enough surface free energy from your > solder mask to prevent dewetting. Sorry for my ignorance, but what is "enough surface free energy"? How do I determine that? >* Bake a board
Electronics Forum | Mon Feb 27 13:02:13 EST 2006 | masrimhd
Hi, Thank you for your answers. But I want to explain some points on which I would appreciate any comment: * Having calibrated the process, we intend to carry out the ROSE test just on SAMPLES of the finished boards. Lets say one every hour. I exp
Electronics Forum | Thu Nov 20 17:30:55 EST 2014 | gregcr
Hi All, I have a customer with a very dense design (24 layers, 0201's lots of micro-BGA and lead-less), and they run extreme data rates. Every once and a while they will have a unit that has some speed fall off and they attribute that to the possib
Electronics Forum | Fri Jun 04 17:26:11 EDT 1999 | C.K.
| | | | Geez, those test guys are always whining about via holes, aren't they? I even had one test guy go over to our finals/add-on department and instruct everone to look for unfilled vias and fill them by hand! Without consulting the area manage
Electronics Forum | Mon Jun 07 11:10:56 EDT 1999 | Brian Wycoff
| | | | | | | Geez, those test guys are always whining about via holes, aren't they? I even had one test guy go over to our finals/add-on department and instruct everone to look for unfilled vias and fill them by hand! Without consulting the area
Electronics Forum | Thu Jul 01 10:24:31 EDT 2004 | davef
There is no specification for �Ion Chromatography for Ionic Cleanliness�. The performance of your product in your customer use environment determines the level that you select. The good part for you is that have at least one pole that you can put i
Electronics Forum | Sun May 30 18:52:35 EDT 1999 | Graham Naisbitt
| | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a
Electronics Forum | Thu May 26 16:41:00 EDT 2011 | scottp
Here's what I do: - Test Surface Insulation Resistance (we're in the high reliability market and use a test significantly harder than IPC's). I also test SIR in combination with other assembly materials like conformal coatings and wave solder flux