Solder Mask Bubbling off after Wave Soldering

Subscribe to Thread

We have been experiencing intermittent problems with the so... - Apr 03, 2000 by

It's a typical answer from a board fabricator - 'None of ou... - Apr 04, 2000 by

Brian, I agree with Jesper, You seem to have a PCB supplie... - Apr 04, 2000 by RDR

Brian G

#4529

Solder Mask Bubbling off after Wave Soldering | 3 April, 2000

We have been experiencing intermittent problems with the solder masking bubbling up from the bottom side of the board, after wave soldering. Our board fabricator claims that none of his other customers are experiencing this problem, and that it is probably due to excessive preheat temperature. I have put in a call to the manufacturer of the solder mask they use, in order to get a spec sheet on the recommended temperature range. (All copper is bare prior to solder masking - so having tin plating under the solder mask is not the culprit.) I have also put in a call to the wave solder machine manufacturer for help, but haven't heard back yet.

We have a two stage preheater; Zone 1 is set for 769 F and Zone 2 is at 360 F (measured at the thermocouples near ceramic glass top that protects quartz-heater tubes). With temperature dots we measured the board top surface, after passing through the preheater, to be between 210 - 220 F. The solder pot temperature is at 500 F.

Question: Do these preheater settings seem so far off as to cause intermittent solder mask problems to the bottom side of boards?

We use a fixture with adjustable rails and fingers during the wave soldering process. It has been noted that a majority of the problems with bubbling/peeling solder mask occurs near the edges, of the bottom side, of the board where the fingers and rails grip the board. One thought was that leftover flux residue on the fingers/rails might be reacting with the solder mask and causing an adverse reaction during the heating process. Of course, when we last used a brand new fixture, we still noticed the problem (even in areas not touched by the fixture).Thus, we are bringing in the rep for the flux manufacturer for suggestions/solutions, as well. We drain/clean the flux pot once a week, but I am not sure if we maintain the proper flux density, upon refilling.

As you can see, we are trying to tackle this problem from all angles. Unfortunately, we are not experts in wave soldering.

Any assistance would be greatly appreciated.

reply »

Jesper K

#4530

Re: Solder Mask Bubbling off after Wave Soldering | 4 April, 2000

It's a typical answer from a board fabricator - 'None of our other customers have these problems'. But, and correct me if I'm wrong, none of the other customers uses the same PCB's as you do!

Your preheat-parameters looks OK - they should not be giving you troubles. Your solder pot temp. should be decreased to between 482 - 491 F - but again it should not affect the soldermask.

The problem you describe about the fingers is pretty logical - if, which I think is the problem, the solder mask has not been hardened sufficiently or the thickness of the mask is insufficient the mask will, because of the mechanical pressure from the fingers, be damaged.

The thing you should do is to contact the board fabricator or an other company that is able to measure the thickness of the soldermask and then ask the board fabricator to prove that his processes where running as expected at the time your boards where fabricated.

Anyway - you shall not take 'It's not my fault' for an answer.

reply »

RDR

#4531

Re: Solder Mask Bubbling off after Wave Soldering | 4 April, 2000

Brian, I agree with Jesper, You seem to have a PCB supplier problem! The conditions that you are processing your assembly with are nothing unusual and in fact very standard throughout all of the manufacturing facilities that I have been in, unless you are using some kind of top secret flux that I have never seen the likes of that would interact with the mask. Have you inspected your PCBs for any delamination issues?

Good Luck

Russ

reply »