Effect of Multiple Reflow Cycles on Intermetallic Compound Creation
Published: |
November 29, 2022 |
Author: |
Václav Wirth, Karel Rendl, and František Steiner |
Abstract: |
This paper deals with the effect of the solder profile and multiple reflow cycles on intermetallic compound (IMC) creation. Soldered joints between PCB and 1206 size chip resistors were made from SAC 305 or SnBi solder alloy. Samples were reflowed one to six times with one of the two different soldering profiles for each soldering alloys. The thickness and composition of IMC layers were measured and observed with a scanning electron microscope. The growing of IMC layers thickness was observed. The results are presented depending on greater value of heating factor and number of reflow cycles. The shear forces for the components were measured and the fracture interfaces were inspected. ... |
|
|
|
|
|
|
You must be a Company Information:
More SMT / PCB assembly technical articles »
- Mar 19, 2024 - What is Underfill | GPD Global
- Mar 19, 2024 - Made in Japan: Solder Paste Jet Dispensing Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 26, 2024 - Precision Control in Electronic Assembly: Selective Wave Soldering Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 02, 2024 - Maximizing Efficiency: The High-Speed SMT Line With Laser Depanelizer | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Dec 27, 2023 - Revolutionizing Tech: SMT Auto IC Programming Machine Mastery | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Browse Technical Library »
Effect of Multiple Reflow Cycles on Intermetallic Compound Creation article has been viewed 383 times